Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility

Chongqing Leomed Technology Co., Ltd.
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now
    Buy cheap Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility from wholesalers
     
    Buy cheap Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility from wholesalers
    • Buy cheap Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility from wholesalers
    • Buy cheap Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility from wholesalers
    • Buy cheap Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility from wholesalers
    • Buy cheap Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility from wholesalers

    Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility

    Ask Lasest Price
    Brand Name : LEOTECH
    Model Number : UT-ML
    Certification : CE
    Price : $39.58/piece
    Payment Terms : T/T
    • Product Details
    • Company Profile

    Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility

    Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility
    UT-ML Dental Zirconia Block
    ● High Strength ● High Transparency ● Natural

    Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility

    Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility





    UT-ML: Superior Zirconia for Demanding Restorations
    Outperforms standard grades:

    • High Translucency: 53% (1 mm)

    • Low Thermal Expansion: (10.5 ± 0.5) × 10⁻⁶ K⁻¹

    • Aging Resistance: <5% monoclinic phase post-acceleration
      Perfect for aesthetic anterior crowns and bridges.


    Product Parameters:
    ModelUT Multilayer 95mm
    Size95mm
    Strength600-800 MPa
    Shades16 VITA Classical.
    Disc Sizes9 thicknesses(10,12.14.16.18.20.22.25.30mm)



    Technical Parameters:

    1.Chemical composition

    ComponentsUT-ML
    ZrO2+HfO2+Y2O3≥99%
    Y2O38.0%-10.0%
    Al2O3<0.15%
    Other Oxides<0.5%

    2.Physical characteristics

    PropertiesUT-ML
    Density before sintering(g.cm-3)3.15±0.05
    Density after sintering(g.cm-3)6.06±0.02
    CTE(25-500℃)(K-1)(10.5±0.5)×10-6
    Flexural strength after sintering(Mpa)600-800
    Translucency(1.0±0.02mm)49%-53%
    Fracture toughness(MPa.m1/2)3.5-5.0
    Hardness(HV10)1150-1250
    Accelerated aging surface monoclinic phase content<5%
    Chemical solubility after sintering(μg.cm-2)<100
    Cytotoxicity0 Level
    Radioactivity(Bq.g-1)<0.1
    Sintering temperature(℃)1480-1510
    Recommend 1500

    Indications For Use ≤3 units



    Sintering:









    Quality Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis &lt;100μg/cm² Solubility for sale
    Inquiry Cart 0
    Send your message to this supplier
     
    *From:
    *To: Chongqing Leomed Technology Co., Ltd.
    *Subject:
    *Message:
    Characters Remaining: (0/3000)